| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 130 |
| Density | g mL-1 | 1.18 - 1.19 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 5.9 - 10.1 (7.5) |
| Heat Deflection Temperature, 0.5 MPa | °C | 76 - 102 |
| Heat Deflection Temperature, 1.8 MPa | °C | |
| Thermal Conductivity | W / mK | 0.19 - 0.22 |
| Rockwell Hardness, M Scale | n/a | M60 - M93 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | |
| Tensile Strength, Break at 23 C | MPa | 59 - 70 |
| Elongation, Yield | % | |
| Elongation, Break | % | 0.5 - 5.0 |
| Tensile Modulus at 23 C | MPa | 1035 - 4825 (3100) |
| Flexural Strength, Yield | MPa | 94 - 103 |
| Flexural Modulus | MPa | 2830 - 3100 |
| Compressive Strength | MPa | |
| Izod Notched | J / m | 16 - 21 |
| Izod Unnotched | J / m |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 1.0 - 3.0 | |
| Dielectric Constant @ 1 MHz | n/a | 2.2 - 3.9 (2.8) | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 0.025 - 0.045 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 115 - 300 (150) | |
| Mold Shrinkage | % | 0.003 - 0.007 | |
| Continuous Service Temperature | °C | 63 - 102 | |
| Water Absorption, 24 hr. Immersion | % | 0.3 - 0.4 |